Quality problems in the production process of seamless steel pipes – quality defects in steel pipe sizing (reduction) and their prevention

The purpose of steel pipe sizing (reduction) is to size (reduce) the rough pipe with a larger diameter to the finished steel pipe with a smaller diameter and to ensure that the outer diameter and wall thickness of the steel pipe and their deviations meet the relevant technical requirements.

The quality defects caused by sizing (reduction) of steel pipes mainly include geometric dimension deviation of steel pipes, sizing (reduction) “blue line”, “nail mark”, scars, abrasions, pockmarks, inner convexity, inner squareness, etc.
Geometric dimension deviation of steel pipes: Geometric dimension deviation of steel pipes mainly refers to the outer diameter, wall thickness, or ovality of steel pipes after sizing (reduction) not meeting the dimension and deviation requirements specified in the relevant standards.

Out-of-tolerance of outer diameter and ovality of steel pipe: The main reasons are: improper roller assembly and hole adjustment of the sizing (reducing) mill, unreasonable deformation distribution, poor processing accuracy, or severe wear of the sizing (reducing) roller, too high or too low temperature of the rough pipe, and uneven axial temperature. It is mainly reflected in the hole shape and roller assembly, the diameter reduction of the rough pipe, and the heating temperature of the rough pipe.

Out-of-tolerance of steel pipe wall thickness: The wall thickness of the rough pipe produced after sizing (reducing) is out of tolerance, which is mainly manifested as uneven wall thickness and non-circular inner hole of the steel pipe. It is mainly affected by the wall thickness accuracy of the rough pipe, the hole shape and hole adjustment, the tension during sizing (reducing), and the size of the rough pipe diameter reduction, as well as the heating temperature of the rough pipe.

“Blue lines” and “fingernail marks” on steel pipes: “Blue lines” on steel pipes are caused by the misalignment of the rollers in one or several frames of the sizing (reducing) mill, which results in the hole being not “round” and the edge of a certain roller cutting into the surface of the steel pipe to a certain depth. “Blue lines” run through the outer surface of the entire steel pipe in the form of one or more lines. “Fingernail marks” are caused by a certain difference in the linear speed between the roller edge and other parts of the groove, which causes the roller edge to stick to the steel and then scratch the surface of the steel pipe. This defect is distributed along the longitudinal direction of the tube body, and its morphology is a short arc, similar to the shape of a “fingernail”, so it is called a “fingernail mark”. “Blue lines” and “fingernail marks” can cause the steel pipe to be scrapped when they are serious. To eliminate the “blue lines” and “fingernail marks” defects on the surface of the steel pipe, the hardness of the sizing (reducing) roller must be guaranteed and its cooling must be kept good. When designing the roll hole or adjusting the roll hole, it is necessary to ensure the appropriate hole side wall opening angle and roll gap value to prevent the hole from being misaligned. In addition, the reduction amount of the single-frame hole should be properly controlled to avoid excessive expansion of the rough pipe in the hole when rolling the low-temperature rough pipe, causing the metal to squeeze into the roll gap of the roll, and damage the bearing due to excessive rolling pressure. Practice shows that the use of tension reduction technology is conducive to limiting the lateral expansion of the metal, which has a very positive effect on reducing the “blue lines” and “fingernail marks” defects of steel pipes.

Steel pipe scarring: The scars of steel pipes are distributed in irregular forms on the surface of the pipe body. Scars are mainly caused by steel sticking to the surface of the sizing (reducing) roller. It is related to factors such as the hardness and cooling conditions of the rollers, the depth of the hole type, and the sizing (reducing) amount of rough pipes. Improving the material of the rollers, increasing the roller surface hardness of the rollers, ensuring good roller cooling conditions, reducing the sizing (reducing) amount of rough pipes, and reducing the relative sliding speed between the roller surface and the metal surface are conducive to reducing the chance of roller sticking to steel. Once scars are found on the steel pipe, the frame where the scars are produced should be found according to the shape and distribution of the defects, and the parts of the rollers that stick to the steel should be inspected, removed, or repaired. Rollers that cannot be removed or repaired should be replaced in time.

Scratches on steel pipes: Scratches on steel pipes are mainly caused by the “ears” between the sizing (reducing) frames and the surfaces of the inlet guide tube or the outlet guide tube sticking to the steel, rubbing and damaging the surface of the moving steel pipe. Once scratches on the surface of the steel pipe are found, Check the guide tube for sticky steel or other attachments in time, or remove the iron “ears” between the sizing (reducing) machine frames.

Outer hemp surface of steel pipe: The outer hemp surface of steel pipe is caused by the wear of the roller surface and becomes rough, or the temperature of the rough pipe is too high, so that the surface oxide scale is too thick, but it is not well removed. Before the rough pipe is sized (reduced), the oxide scale on the outer surface of the rough pipe should be removed promptly and effectively with high-pressure water to reduce the occurrence of defects on the outer hemp surface of the steel pipe.

Inner convexity of steel pipe: The inner convexity of steel pipe refers to the fact that when the rough pipe is sized (reduced), due to the excessive sizing (reducing) amount of the single frame of the sizing (reducing) machine, the pipe wall of the steel pipe is bent inward (sometimes in a closed shape), and a raised linear defect is formed on the inner wall of the steel pipe. This defect does not occur often. It is mainly caused by errors in the combination of the roller frames of the sizing (reducing) machine when sizing (reducing) thin-walled steel pipes. Or serious errors in hole type adjustment, or mechanical failure of the frame. Increasing the tension coefficient can increase the critical diameter reduction. Under the same diameter reduction conditions, it can effectively avoid the internal resistance of the steel pipe. Reducing the diameter reduction can improve the stability of the rough pipe during deformation and effectively prevent the steel pipe from convex. In production, the roll matching should be carried out strictly according to the rolling table, and the roll hole type should be carefully adjusted to prevent the occurrence of convex defects in the steel pipe.

“Inner square” of steel pipe: “Inner square” of steel pipe means that after the rough pipe is sized (reduced) by the sizing (reducing) mill, the inner hole of its cross-section is “square” (two-roller sizing and reducing mill) or “hexagonal” (three-roller sizing and reducing mill). The “inner square” of the steel pipe will affect its wall thickness accuracy and inner diameter accuracy. The “inner square” defect of the steel pipe is related to the D/S value of the rough pipe, the diameter reduction, the tension during the sizing (reduction), the hole shape, the rolling speed, and the rolling temperature. When the D/S value of the rough pipe is smaller, the tension is smaller, the diameter reduction is larger, and the rolling speed and rolling temperature are higher, the steel pipe is more likely to have uneven transverse wall thickness, and the “inner square” defect is more obvious.